Method for producing black-plated steel sheet, and method for producing molded article of black-plated steel sheet

ABSTRACT

The present invention pertains to a method for producing a black-plated steel sheet capable of being blackened in a short amount of time, and exhibiting an excellent ability to maintain a black appearance after processing. As an original sheet, the sheet used is a Zn-plating steel sheet which contains molten Al and Mg and has a Zn-plating layer containing molten Al and Mg, containing Al in the amount of 0.1-22.0 mass %, inclusive, and containing Mg in the amount of 0.1-1.5 mass %, inclusive. The plating layer is blackened by causing the molten-plating steel sheet to contact water vapor inside a tightly sealed container. When doing so, the concentration of oxygen inside the tightly sealed container is 13% or less.

TECHNICAL FIELD

The present invention relates to a method for producing a black-plated steel sheet and a method for producing a formed article of the black-plated steel sheet.

BACKGROUND ART

In the field such as roofing materials and exterior materials of a building, home appliances and automobiles, the needs for steel sheets having a black appearance is increasing from the viewpoints of design and so on. The surface of a steel sheet may be blackened by applying a black coating material to the surface of a steel sheet so as to form a black coating film. In the field described above, however, steel sheets with plating such as hot-dip Zn-plating, hot-dip Al-containing Zn-plating, and hot-dip Al and Mg-containing Zn-plating are used in many cases from the viewpoint of corrosion resistance. The plated steel sheet has a metallic gloss surface with silver gray color. Accordingly, in order to obtain a black appearance of quality design by application of a black coating material, a thick coating film is required to conceal the color of the plated steel sheet, resulting in high coating costs. Furthermore, the thick coating film precludes resistance welding such as spot welding, which is another disadvantage.

As a method for concealing the metallic gloss with silver gray color of a plated steel sheet without formation of a black coating film, a method for blackening a plating layer itself has been proposed (e.g. refer to PTL 1). PTL 1 discloses a method for forming a thin black layer at the plating layer surface by blowing high-temperature water vapor onto a hot-dip Al-containing Zn-plated steel sheet for 24 hours or more.

CITATION LIST Patent Literature PTL 1

-   Japanese Patent Application Laid-Open No. SHO 64-56881

SUMMARY OF INVENTION Technical Problem

A problem in the method for producing a black-plated steel sheet described in PTL 1 is that when the plating layer is blackened over the whole thickness, the plating layer is embrittled to lower the adhesion and therefore a thick black layer cannot be formed. Therefore, in the black-plated steel sheet produced by the production method described in PTL 1, when the surface of the plating layer is scratched by processing or the like, silvery-white color being the color of the plating layer itself is exposed, which deteriorates the surface appearance, and therefore the black-plated steel sheet cannot stand intense processing. Furthermore, another problem in the method for producing a black-plated steel sheet described in PTL 1 is that the blackening treatment requires a long time.

An object of the present invention is to provide a method for producing a black-plated steel sheet capable of being blackened in a short time and exhibiting an excellent ability to maintain a black appearance after processing. Moreover, another object of the present invention is to provide a method for producing a formed article of the black-plated steel sheet.

Solution to Problem

The present inventors have found that the problems can be solved by using, as an original plate, a hot-dip Al and Mg-containing Zn-plated steel sheet including a hot-dip Al and Mg-containing Zn-plated layer which includes 0.1 mass % or more and 22.0 mass % or less of Al and 0.1 mass % or more and less than 1.5 mass % of Mg and contacting the plated steel sheet with water vapor in a closed vessel, and have made further studies to complete the present invention.

Namely, the first of the present invention relates to the following method for producing a black-plated steel sheet.

[1] A method for producing a black-plated steel sheet including: providing a hot-dip Al and Mg-containing Zn-plated steel sheet including a hot-dip Al and Mg-containing Zn-plated layer which includes 0.1 mass % or more and 22.0 mass % or less of Al and 0.1 mass % or more and less than 1.5 mass % of Mg; and contacting the hot-dip Al and Mg-containing Zn-plated steel sheet with water vapor in a closed vessel, in which an oxygen concentration in the closed vessel is 13% or less.

[2] The method for producing a black-plated steel sheet according to [1], further including forming an inorganic coating film on a surface of the hot-dip Al and Mg-containing Zn-plated steel sheet.

[3] The method for producing a black-plated steel sheet according to [2], wherein the inorganic coating film includes one or more compounds selected from the group consisting of an oxide of valve metal, an oxoate of valve metal, a hydroxide of valve metal, a phosphate of valve metal, and a fluoride of valve metal.

[4] The method for producing a black-plated steel sheet according to [3], wherein the valve metal is one or more metals selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, W, Si, and Al.

[5] The method for producing a black-plated steel sheet according to [1], further including forming an organic resin coating film on a surface of the hot-dip Al and Mg-containing Zn-plated steel sheet.

[6] The method for producing a black-plated steel sheet according to [5], wherein an organic resin comprised in the organic resin coating film is urethane-based resin obtained by the reaction of polyols including an ether-based polyol and an ester-based polyol with polyisocyanate, a proportion of the ether-based polyol in the polyols being 5 to 30 mass %.

[7] The method for producing a black-plated steel sheet according to [6], in which the organic resin coating film further includes a polyvalent phenol.

[8] The method for producing a black-plated steel sheet according to any one of [5] to [7], in which the organic resin coating film includes a lubricant.

[9] The method for producing a black-plated steel sheet according to any one of [5] to [8], in which the organic resin coating film includes one or more compounds selected from the group consisting of an oxide of valve metal, an oxoate of valve metal, a hydroxide of valve metal, a phosphate of valve metal, and a fluoride of valve metal.

[10] The method for producing a black-plated steel sheet according to [9], in which the valve metal is one or more metals selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, W, Si, and Al.

[11] The method for producing a black-plated steel sheet according to any one of [5] to [10], in which the organic resin coating film is a laminate layer or a coating layer.

[12] The method for producing a black-plated steel sheet according to any one of [5] to [11], in which the organic resin coating film is a clear coating film.

Moreover, the second of the present invention relates to the following method for producing a formed article of a black-plated steel sheet.

[13] A method for producing a formed article of a black-plated steel sheet, including: providing a hot-dip Al and Mg-containing Zn-plated steel sheet including a hot-dip Al and Mg-containing Zn-plated layer which includes 0.1 mass % or more and 22.0 mass % or less of Al and 0.1 mass % or more and less than 1.5 mass % of Mg; contacting the hot-dip Al and Mg-containing Zn-plated steel sheet with water vapor in a closed vessel; and forming the hot-dip Al and Mg-containing Zn-plated steel sheet before or after contacting the hot-dip Al and Mg-containing Zn-plated steel sheet with the water vapor, in which an oxygen concentration in the closed vessel is 13% or less.

Advantageous Effects of Invention

According to the present invention, a black-plated steel sheet having a black appearance excellent in design property, the black-plated steel sheet exhibiting an excellent ability to maintain a black appearance after processing and a formed article thereof can be produced in a short time. The produced black-plated steel sheet of the present invention is excellent in design, retention of the black appearance, press formability and corrosion resistance, being applicable as a plated steel sheet for, for example, roofing materials and exterior materials of a building, home appliances, and automobiles.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1A is a scanning electron microscopic image illustrating a cross section of a plating layer of a hot-dip Al and Mg-containing Zn-plated steel sheet before water vapor treatment, and FIG. 1B is a scanning electron microscopic image illustrating a cross section of a plating layer of a hot-dip Al and Mg-containing Zn-plated steel sheet after water vapor treatment; and

FIG. 2 is a schematic diagram illustrating a laminated state of plated steel sheets and spacers in Experimental Example 3.

DESCRIPTION OF EMBODIMENTS

1. Method for Producing Black-Plated Steel Sheet

The production method of a black-plated steel sheet of the present invention includes: 1) a first step of providing a hot-dip Al and Mg-containing Zn-plated steel sheet; and 2) a second step of contacting the Al and Mg-containing Zn-plated steel sheet with water vapor in a closed vessel. The method may further include: 3) a third step of forming an inorganic coating film or organic resin coating film on the surface of the hot-dip Al and Mg-containing Zn-plated steel sheet, before or after the second step as an optional step.

[First Step]

A hot-dip Al and Mg-containing Zn-plated steel sheet in which a hot-dip Al and Mg-containing Zn-plated layer (hereinafter also referred to as “plating layer”) is formed on a surface of a base material steel sheet is prepared in the first step.

(Base Material Steel Sheet)

The kind of the base material steel sheet is not particularly limited. As a base material steel sheet, for example, a steel sheet including low carbon steel, medium carbon steel, high carbon steel, alloy steel, or the like can be used. In the case where a favorable press formability is required, a steel sheet for deep drawing including low carbon Ti-added steel, low carbon Nb-added steel, or the like is preferable as a base material steel sheet. Moreover, a high strength steel sheet in which P, Si, Mn, or the like is added may be used.

(Hot-Dip al and Mg-Containing Zn-Plated Layer) As an original plate to be used in the production method of the present invention, a hot-dip Al and Mg-containing Zn-plated steel sheet including a hot-dip Al and Mg-containing Zn-plated layer which includes 0.1 mass % or more and 22.0 mass % or less of Al and 0.1 mass % or more and less than 1.5 mass % of Mg is used. Al and Mg are elements that improve corrosion resistance of a Zn based-plated steel sheet, and are essential elements for conducting blackening in the present invention as will be described later. In the case where the Al content or the Mg content is smaller than the lower limit value, sufficient corrosion resistance is not obtained. On the other hand, in the case where the Al content or the Mg content is larger than the upper limit value, a beautiful plated steel sheet cannot be obtained due to excessive generation of oxides (dross) at a plating bath surface during production of the plated steel sheet.

It sometimes occurs that the hot-dip Al and Mg-containing Zn-plated layer having the above-described composition contains a single phase of Al as a metallic structure depending on the plating composition. For example, the single phase of Al is a primary Al″. Al is an element that forms an amphoteric oxide and has a higher reactivity with H₂O when compared with Zn and Mg. Thus, metal Al immediately becomes an oxide or hydrated oxide by the following reaction when the metal Al is contacted with high temperature water vapor. In the present specification, an oxide and a hydrated oxide are collectively referred to as an oxide. In the black-plated steel sheet described in PTL 1, since Zn that is poor in reactivity mainly reacts with H₂O, the oxidation reaction requires much time. On the other hand, in the black-plated steel sheet of the present invention, since Al that is rich in reactivity reacts with H₂O as will be described later, the time required for the oxidation reaction is short.

2Al+(3+n)H₂O→Al₂O₃ .nH₂O+3H₂

The hot-dip Al and Mg-containing Zn-plated layer having the above-described composition includes at least one or more of a primary Al″, a Zn primary crystal, a Zn₂Mg primary crystal, a Zn/Al binary eutectic structure, an Al/Zn₂Mg binary eutectic structure, a Zn/Zn₂Mg binary eutectic structure, and an Al/Zn/Zn₂Mg ternary eutectic structure. For example, in the hot-dip Al and Mg-containing Zn-plated layer illustrated in FIG. 1A, the Al/Zn/Zn₂Mg ternary eutectic structure (in the figure, represented as “Al/Zn/Zn₂Mg”) and the single phase of Al (in the figure, represented as “primary crystal Al phase” are mixed.

As illustrated in FIG. 1A, respective phases (Al phase, Zn phase, and Zn₂Mg phase) that form the Al/Zn/Zn₂Mg ternary eutectic structure each have an irregular size and shape, and are complicated with one another. The Zn phase (the region showing a light gray color in the ternary eutectic structure in FIG. 1A) in the Al/Zn/Zn₂Mg ternary eutectic structure is a Zn solid solution containing a small amount of Al, and in some cases further containing a small amount of Mg. The Zn₂Mg phase in the ternary eutectic structure (the region showing dark gray color in the ternary eutectic structure in FIG. 1A and the region distributed in a lamellar form between the Zn phases) is an intermetallic compound phase that is present near the point where Zn accounts for about 84 mass % in a Zn—Mg binary equilibrium diagram.

Moreover, the Al phase and the Al phase of the primary crystal in the ternary eutectic structure are derived from an Al″ phase (Al solid solution that contains Zn and includes a small amount of Mg) at a high temperature in an Al—Zn—Mg ternary equilibrium diagram. The Al″ phase at a high temperature usually appears as a fine Al phase and a fine Zn phase separately at normal temperature. The fine Al phase and the fine Zn phase in the ternary eutectic structure are dispersed in the Zn₂Mg phase.

(Production of Hot-Dip al and Mg-Containing Zn-Plated Steel Sheet)

The hot-dip Al and Mg-containing Zn-plated steel sheet can be produced by, for example, preparing a hot-dip plating bath including 0.1 mass % or more and 22.0 mass % or less of Al, 0.1 mass % or more and less than 1.5 mass % of Mg, and the balance of Zn, dipping a base material steel sheet in the hot-dip plating bath, and then pulling up the base material steel sheet to apply hot-dip plating on the surface of the base material steel sheet.

Moreover, Si that can suppress the growth of an Al—Fe alloy layer at an interface of the base material steel sheet and the plating layer may be added to the plating bath in a range of 0.005 mass % to 2.0 mass % in order to improve the adhesion of the base material steel sheet with the plating layer. In the case, it sometimes occurs that an Mg₂Si phase is observed as a metal structure in the plating layer. When the concentration of Si exceeds 2.0 mass %, there is a risk that a Si-based oxide that inhibits blackening is generated at the surface of the plating layer.

Moreover, Ti, B, Ti—B alloy, a Ti-containing compound, or a B-containing compound may be added to the plating bath in order to suppress the generation and growth of a Zn₁₁Mg₂ phase that gives an adverse influence on the appearance and the corrosion resistance. It is preferable to set the amount of these compounds added so as to be within a range of 0.001 mass % to 0.1 mass % for Ti, and within a range of 0.0005 mass % to 0.045 mass % for B. When Ti or B is added in an excessive amount, there is a risk that a precipitate is grown in the plating layer. In addition, the addition of Ti, B, Ti—B alloy, the Ti-containing compound, or the B-containing compound gives little influence on blackening by water vapor treatment.

In addition, in the present specification, the content value of each component in the plating layer is a value obtained by dividing the mass of each metal component contained in the plating layer by the mass of the whole metals contained in the plating layer and expressed by percentage. Namely, the mass of oxygen and the mass of water contained in the oxides or hydrated oxides are not included as a component in the plating layer. Thus, in the case where the elution of a metal component during the water vapor treatment does not occur, the content value of each component in the plating layer before and after the water vapor treatment does not change.

The thickness of the plating layer is not particularly limited, however, it is preferable that the thickness of the plating layer is within a range of 3 to 100 μm. In the case where the thickness of the plating layer is less than 3 μm, a scratch that reaches the base material steel sheet during handling is liable to occur, and therefore there is a risk that the corrosion resistance and the ability to maintain a black appearance are lowered. On the other hand, when the thickness of the plating layer exceeds 100 μm, there is a risk that the plating layer and the base material steel sheet are separated at a processed part because the ductility of the plating layer is different from the ductility of the base material steel sheet when the plating layer and the base material steel sheet are subjected to compression.

[Second Step]

The plated steel sheet prepared in the first step is contacted with water vapor in a closed vessel to blacken the plating layer in the second step. In the present specification, contacting the hot-dip Al and Mg-containing Zn-plated steel sheet with water vapor in a closed vessel is referred to as “water vapor treatment.” By the water vapor treatment, it is possible to lower the surface lightness (L* value) of the plating layer to 60 or less (preferably 40 or less, further preferably 35 or less). The surface lightness (L* value) of the plating layer is measured by a spectral reflection measuring method in accordance with JIS K 5600 using a spectroscopic color-difference meter.

When the plated steel sheet is contacted with water vapor in the second step, a black oxide is generated in the plating layer. Here, “in the plating layer” includes both of the surface of the plating layer and the inside of the plating layer. The mechanism by which the black oxide is generated is not particularly limited, however it is inferred as follows.

An oxide of Al being an easily oxidizable element is present at the surface of the plating layer. When the water vapor treatment is started, an oxidation layer at the surface reacts with H₂O to be changed to a hydrated oxide in the first place, and H₂O having passed through the oxide layer reacts with a metal in the plating layer. At this time, Zn that is present in the largest amount in the plating layer is oxidized to become an oxide or a hydrated oxide. In the present specification, an oxide and a hydrated oxide are collectively referred to as an oxide. The oxidation of Zn progresses in a depth direction of the plating layer as time passes. In this state, when Al that has a high reactivity with oxygen is present near the Zn oxide, since oxygen potential is lowered by the water vapor atmosphere, Al that has a high reactivity deprives the Zn oxide of oxygen to become an Al oxide. Therefore, it is considered that the Zn oxide is changed to an oxygen deficient-type oxide (for example, ZnO_(1-x) and so on) with nonstoichiometric composition. Moreover, since the oxygen potential is low, it is considered that a part of the Al oxide also becomes an oxygen deficient-type oxide. When the oxygen deficient-type Zn oxide is generated as described here, light is trapped in the defect level, and therefore the oxide shows a black appearance.

In the production method of PTL 1, only the surface of the plating layer is blackened due to the generation of a needle crystal of ZnO_(1-x). On the other hand, in the production method of the present invention, a black oxide layer is formed at the surface of the plating layer, and the black oxide is dispersed inside the plating layer, taking the aforementioned reaction mechanism into consideration. Thus, in the black-plated steel sheet produced by the production method of the present invention, even when a scratch occurs in the plating layer by processing, the black appearance is maintained. The blackened oxides in the interior of the plating layer can be confirmed by optical microscopic observation of the cross section of a plating layer, or by amalgamating metals Zn, Al and Mg in a plating layer with saturated HgCl₂ solution for removal and collecting oxides only. In addition, the black oxide dispersed in the plating layer may be blackened to the inside thereof or only at the surface thereof.

When oxygen is present in the atmosphere in conducting the water vapor treatment in the second step, blackening cannot sufficiently be conducted. It is inferred that this is because when the water vapor treatment is conducted in the atmosphere where a large amount of oxygen is contained, the formation of basic zinc aluminum carbonate showing gray color at the surface layer has priority over the formation of the oxygen deficient-type Zn oxide showing black color. In the second step, therefore, it is necessary to reduce the oxygen concentration in the atmosphere (oxygen partial pressure) for water vapor treatment. Specifically, it is preferable that the oxygen concentration during the water vapor treatment is 13% or less. The method for reducing the oxygen concentration in the atmosphere is not particularly limited. For example, the water vapor concentration (relative humidity) may be raised, the air in the vessel may be replaced with an inert gas, or the air in the vessel may be removed by a vacuum pump or the like. In any of the cases, it is necessary that the water vapor treatment is conducted in a closed vessel.

(Treatment Temperature)

It is preferable that the temperature for the water vapor treatment is within a range of 50° C. or more and 350° C. or less. When the temperature for the water vapor treatment is less than 50° C., the rate of blackening is slow and the productivity is lowered. Moreover, when water is heated to 100° C. or more in the closed vessel, the pressure in the vessel becomes 1 atmospheric pressure or higher and the oxygen concentration in the atmosphere can easily be reduced, and therefore it is more preferable that the temperature for the water vapor treatment is 100° C. or more. On the other hand, when the temperature for the water vapor treatment exceeds 350° C., the control of the blackening rate becomes difficult due to an extremely high blackening rate. Moreover, when the temperature for the water vapor treatment exceeds 350° C., not only a large-sized treatment apparatus is required, but also the total treatment time including the treatment time required for raising and reducing temperature becomes long, which is not practical. Thus, it is particularly preferable from the standpoints of removal of oxygen in the atmosphere and control of the rate of blackening that the temperature for the water vapor treatment is within a range of 100° C. or more and 200° C. or less.

In the case where the temperature for the water vapor treatment is desired to be reduced to less than 100° C., an inert gas may be put into the vessel in order to suppress the mixing of oxygen by setting the pressure in the vessel to atmospheric pressure or higher. The kind of the inert gas is not particularly limited as long as the inert gas has no relation to the blackening reaction. Examples of the inert gas include Ar, N₂, He, Ne, Kr, and Xe. Among these inert gases, Ar, N₂, and He that are available at low cost are preferable. Moreover, the water vapor treatment may be conducted after removing the air in the vessel by a vacuum pump or the like.

(Relative Humidity)

It is preferable that the relative humidity of water vapor during the water vapor treatment is within a range of 30% or more and 100% or less, more preferably within a range of 30% or more and less than 100%. In the case where the relative humidity of water vapor is less than 30%, the rate of blackening is slow and the productivity is lowered. Moreover, in the case where the relative humidity of water vapor is 100%, there is a risk that poor appearance is liable to occur due to adherence of dew condensation water to the surface of the plated steel sheet.

The treatment time for the water vapor treatment can appropriately be set depending on the conditions of the water vapor treatment (temperature, relative humidity, pressure, and so on), the amount of Al and Mg in the plating layer, required lightness, and so on.

(Preheating)

Moreover, when the plated steel sheet is heated before conducting the water vapor treatment to form Zn₁₁Mg₂ from Zn₂Mg in the plating layer, it is possible to shorten the time for the water vapor treatment for obtaining black appearance of the plating layer. It is preferable that the heating temperature of the plated steel sheet at this time is within a range of 150 to 350° C. In the case where the heating temperature is less than 150° C., the treatment time until Zn₁₁Mg₂ is formed from Zn₂Mg by preheating becomes long, and therefore the merit of shortening the time for the water vapor treatment is not obtained. On the other hand, although a heating temperature higher than 350° C. allows the change of Zn₂Mg to Zn₁₁Mg₂ in a short time, the further progress of reaction may form a plating layer having lower corrosion resistance due to separation of each of the phases with progress of the change in the state of the plated layer, so that the preheating cannot be easily controlled. The treating time of preheating may appropriately be set depending on the treatment temperature, the amount of Al and Mg in the plating layer, and so on. Usually, heating at 250° C. for about 2 hours may be enough. It is considered that the preheating is effective when the Mg content in the plating layer is 0.3 mass % or more, taking it into consideration that the Zn₂Mg phase usually appears when the Mg content in the plating layer is 0.3 mass % or more.

The water vapor treatment may be conducted to any of a plated steel sheet wound in the shape of a coil, a planar plated steel sheet before forming, and a plated steel sheet after conducting forming, welding, or the like.

[Optional Step]

An inorganic coating film or an organic resin coating film is formed on the surface of the hot-dip Al and Mg-containing Zn-plated steel sheet in an optional step which is optionally conducted before or after the second step. The inorganic coating film and the organic resin coating film improve the corrosion resistance and the galling resistance (retention of black appearance) of a black-plated steel sheet.

(Inorganic Coating Film)

The inorganic coating film preferably includes one or more compounds (hereinafter referred to as “valve metal compound”) selected from the group consisting of an oxide of valve metal, an oxoate of valve metal, a hydroxide of valve metal, a phosphate of valve metal, and a fluoride of valve metal. Inclusion of a valve metal compound reduces an environmental load and imparts an excellent barrier function. The valve metal means a metal the oxide of which exhibits high insulation resistance. Examples of the valve metal include one or more metals selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, W, Si, and Al. A known compound may be used as the valve metal compound.

Inclusion of a soluble fluoride of valve metal in an inorganic coating film can impart a self-repairing function. The fluoride of valve metal dissolved in moisture in atmosphere forms oxides or hydroxides having poor solubility, reprecipitating on the steel sheet exposed from defect regions in a coating film so as to bury the defect regions. For inclusion of the soluble fluoride of valve metal in an inorganic coating film, a soluble fluoride of valve metal may be added to the inorganic coating material, or a soluble fluoride such as (NH₄)F may be added in addition to a valve metal compound.

The inorganic coating film may further include a soluble or poorly soluble metal phosphate or complex phosphate. The soluble phosphate eluted from the inorganic coating film to defective regions in a coating film reacts with the metal of a plated steel sheet so as to form an insoluble phosphate, complementing the self-repairing function of valve metal imparted by the soluble fluoride. The poorly soluble phosphate is dispersed in the inorganic coating film so as to improve the strength of the coating film. Examples of the metal contained in the soluble metal phosphate or complex phosphate include an alkali metal, an alkali earth metal and Mn. Examples of the poorly soluble metal phosphate or complex phosphate include Al, Ti, Zr, Hf and Zn.

The inorganic coating film can be formed by a known method. For example, an inorganic coating material including a valve metal compound or the like may be applied on the surface of the hot-dip Al and Mg-containing Zn-plated steel sheet before or after contact with water vapor, and then dried without washing with water. Examples of the coating method include a roll coating method, a spin coating method, and a spraying method. In the case where the valve metal compound is added to the inorganic coating material, an organic acid having chelating function may be added to the inorganic coating material so that the valve metal compound can stably be present in the inorganic coating material. Examples of the organic acid include tannic acid, tartaric acid, citric acid, oxalic acid, malonic acid, lactic acid, and acetic acid.

(Organic Resin Coating Film)

The organic resin for constituting the organic resin coating film may be a urethane-based resin, an epoxy-based resin, an olefin-based resin, a styrene-based resin, a polyester-based resin, an acrylic-based resin, a fluorine-based resin, a combination of these resins, or a copolymer or a modified product of these resins. The use of these organic resins having flexibility prevents occurrence of cracks during production of a black-plated steel sheet, improving the corrosion resistance. Further, the valve metal compounds included in the organic resin film can be dispersed in the organic resin film (organic resin matrix), as described in the following.

Preferably the organic resin coating film includes a lubricant. Inclusion of a lubricant reduces the friction between a mold and the surface of a plated steel sheet during processing such as pressing so that galling of the plated steel sheet can be suppressed (improvement in galling resistance). The type of lubricant is not specifically limited and may be selected from known lubricants. Examples of the lubricants include an organic wax such as a fluorine-based wax, a polyethylene-based wax, and a styrene-based wax, and an inorganic lubricant such as molybdenum disulfide and talc.

Similarly to an inorganic coating film, the organic resin coating film preferably includes the valve metal compounds described above. Inclusion of a valve metal compound reduces an environmental load and imparts excellent barrier function.

Similarly to an inorganic coating film, the organic resin coating film may further include a soluble or poorly soluble metal phosphate or complex phosphate. The soluble phosphate eluted from the organic coating film to defective regions in a coating film reacts with the metal of a plated steel sheet so as to form an insoluble phosphate, complementing the self-repairing function of valve metal imparted by the soluble fluoride. The poorly soluble phosphate is dispersed in the organic coating film so as to improve the strength of the coating film.

The organic resin coating film including a valve metal compound and a phosphate usually allows for formation of an interface reaction layer between a plated steel sheet and the organic resin coating film. The interface reaction layer is a dense layer formed of zinc fluoride, zinc phosphate, and a fluoride of valve metal or a phosphate which are reaction products of a fluoride or a phosphate contained in an organic coating material with metals contained in the plated steel sheet or a valve metal. The interface reaction layer has excellent environment blocking capability, preventing corrosive components in atmosphere from reaching the plated steel sheet. Meanwhile, the organic resin coating film includes particles of oxide of valve metal, hydroxide of valve metal, fluoride of valve metal and phosphate, which are dispersed in an organic resin matrix. Since the particles of oxides of valve metal etc. are three-dimensionally dispersed in an organic resin matrix, the corrosive components such as moisture passing through the organic resin matrix can be captured. As a result, the organic resin coating film substantially reduces corrosive components reaching the interface reaction layer. Owing to the organic resin coating film and the interface reaction layer, excellent anti-corrosion effect can be achieved.

The organic resin coating film may be, for example, a urethane-based resin coating film which contains urethane based resin having excellent flexibility. The urethane-based resin for constituting the urethane-based resin coating film may be obtained by reacting polyol with polyisocyanate. In the case of treating with water vapor for blackening after formation of the urethane-based resin coating film, the polyol for use preferably includes a combination of an ether-based polyol (polyol having an ether bond) and an ester-based polyol (polyol having an ester bond) at a predetermined ratio.

A urethane-based resin coating film formed of ester-based polyol alone as polyol allows ester bonds in the urethane-based resin to be hydrolyzed by water vapor, so that the corrosion resistance cannot be sufficiently improved. On the other hand, a urethane-based resin coating film formed of ether-based polyol alone as polyol has insufficient adhesion to a plated steel sheet, so that the corrosion resistance cannot be sufficiently improved. In contrast, the present inventors found that use of the combination of an ether-based polyol and an ester-based polyol at a predetermined ratio markedly improves the corrosion resistance of a plated steel sheet, with making effective use of the advantages of both an ether-based polyol and an ester-based polyol, and complementing the disadvantages of each other. The effect of the urethane-based resin coating film for improving the corrosion resistance can be thereby maintained even when treated with water vapor to impart black color after formation of the urethane-based resin coating film. A black-plated steel sheet which has black color and excellent corrosion resistance can be thus produced.

The type of the ether-based polyol is not specifically limited, and may be properly selected from known ones. Examples of the ether-based polyol include polyethylene glycol, polypropylene glycol, and a straight chain polyalkylene polyol such as an ethylene oxide or propylene oxide adduct of glycerin.

The type of the ester-based polyol is also not specifically limited, and may be properly selected from known ones. The ester-based polyol for use may be, for example, a linear polyester having a hydroxyl group in a molecular chain which is obtained by the reaction of dibasic acid with low-molecular weight polyol. Examples of the dibasic acid include adipic acid, azelaic acid, dodecanedioic acid, dimer acid, isophthalic acid, hexahydro phthalic anhydride, terephthalic acid, dimethyl terephthalate, itaconic acid, fumaric acid, maleic anhydride, and esters of each of the acids.

The proportion of the ether-based polyol in polyol formed of a combination of an ether-based polyol and an ester-based polyol is preferably in the range of 5 to 30 mass %. A proportion of the ether-based polyol less than 5 mass % results in excessively increased proportion of the ester-based polyol, so that the urethane-based resin coating film is easily hydrolyzed. Consequently the corrosion resistance may not be sufficiently improved. On the other hand, a proportion of the ether-based polyol more than 30 mass % results in excessively increased proportion of the ether-based polyol, so that the adhesion to a plated steel sheet is reduced. Consequently the corrosion resistance may not be sufficiently improved.

The type of polyisocyanate is not specifically limited, and may be properly selected from known ones. The polyisocyanate for use may be, for example, a polyisocyanate compound having an aromatic ring. Examples of the polyisocyanate compounds having an aromatic ring include hexamethylene diisocyanate, o-, m-, or p-phenylene diisocyanate, 2,4- or 2,6-tolylene diisocyanate, 2,4- or 2,6-tolylene diisocyanate having a hydrogenated aromatic ring, diphenylmethane-4,4′-diisocyanate, 3,3′-dimethyl-4,4′-biphenylene diisocyanate, ω,ω′-diisocyanate-1,4-dimethylbenzene, and ω,ω′-diisocyanate-1,3-dimethylbenzene. These may be used alone or may be used in combination of two or more.

Preferably the urethane-based resin coating film further includes a polyvalent phenol. A urethane-based resin coating film including a polyvalent phenol allows for formation of a layer of concentrated polyvalent phenol at the interface between a plated steel sheet and the polyvalent phenol so as to make strong adhesion between them. Accordingly, blending of polyvalent phenol in the urethane-based resin coating film further improves the corrosion resistance of the urethane-based resin coating film.

The type of polyvalent phenol is not specifically limited and may be properly selected from known ones. Examples of the polyvalent phenol include tannic acid, gallic acid, hydroquinone, catechol, and phloroglucinol. The amount of blended polyvalent phenol in the urethane-based resin coating film is preferably in the range of 0.2 to 30 mass %. An amount of the blended polyvalent phenol less than 0.2 mass % has insufficient effect of the polyvalent phenol. On the other hand, with an amount of the blended polyvalent phenol more than 30 mass %, the stability of the coating material may be reduced.

The organic resin coating film may be a coating layer or a laminate layer. The organic resin coating film is preferably a clear coating film for taking advantage of the black appearance of the black-plated steel sheet.

The organic coating film may be formed by a known method. For example, in the case of the organic resin coating film formed of a coating layer, an organic coating material which contains an organic resin and a valve metal etc. may be applied to the surface of a hot-dip Al and Mg-containing Zn-plated steel sheet before or after contact with water vapor, and then dried without washing with water. Examples of the application method include a roll coating method, a spin coating method, and a spray coating method. In the case of adding a valve metal compound to an organic coating material, an organic acid having a chelating function may be added to the organic coating material so that the valve metal compound can stably exist in the organic coating material. In the case of application of an organic coating material which contains an organic resin, a valve metal compound, a fluoride, and a phosphate to the surface of a plated steel sheet, a coating film (interface reaction layer) consisting of a reaction product of inorganic negative ions such as fluorine ions and phosphoric ions with metals contained in the plated steel sheet or a valve metal is preferentially and densely formed on the surface of the plated steel sheet, on which an organic resin coating film including dispersed particles of oxides of valve metal, hydroxides of valve metal, fluorides of valve metal and phosphates is formed. In contrast, in the case of the organic resin coating film formed of a laminate layer, an organic resin film which contains a valve metal or the like may be laminated on the surface of a plated steel sheet.

According to the procedures described above, a plating layer can be blackened to produce a black-plated steel sheet excellent in retention of the black appearance and press formability.

The production method of the present invention uses water vapor for blackening, so that a black-plated steel sheet can be produced without placing a load to the environment.

Moreover, in the black-plated steel sheet obtained by the production method of the present invention, the black oxide imparting a color tone of black is present not only at the surface of the plating layer but also inside the plating layer. Thus, the black-plated steel sheet obtained by the production method of the present invention can maintain the black appearance even when the surface of the plating layer is scraped, and exhibits an excellent ability to maintain a black appearance.

Moreover, in the black-plated steel sheet obtained by the production method of the present invention, the black oxide imparting a color tone of black is dispersed in the plating layer without forming a single film. Thus, the black-plated steel sheet obtained by the production method of the present invention has excellent press formability without reduction in adhesion of the plating layer. As a matter of course, the black-plated steel sheet obtained by the production method of the present invention has an excellent corrosion resistance similar to the corrosion resistance of a usual hot-dip Al and Mg-containing Zn-plated steel sheet.

Moreover, the black-plated steel sheet obtained by the production method of the present invention does not have a coating film, and therefore spot welding can also be conducted in the same manner as in a usual hot-dip Al and Mg-containing Zn-plated steel sheet.

2. Method for Producing Formed Article of Black-Plated Steel Sheet

The method for producing a formed article of the black plated steel sheet of the present invention includes 1) providing a hot-dip Al and Mg-containing Zn-plated steel sheet, 2) contacting the hot-dip Al and Mg-containing Zn-plated steel sheet with water vapor in a closed vessel, and 3) forming the hot-dip Al and Mg-containing Zn-plated steel sheet before or after 2).

[First Step and Second Step]

The above first step and second step are the same as the first step and the second step of the above-described method for producing a black-plated steel sheet.

[Third Step]

The hot-dip Al and Mg-containing Zn-plated steel sheet is formed in the third step which is conducted before or after the second step. Specifically, in the case where the third step is conducted after the second step, the black-plated steel sheet contacted with water vapor is formed to obtain a formed article of the black-plated steel sheet. On the other hand, in the case where the third step is conducted before the second step, the plated steel sheet before being contacted with water vapor is formed. In this case, the formed article of the plated steel sheet is blackened by contacting the formed article of the plated steel sheet with water vapor in the second step conducted after forming.

The method for forming the hot-dip Al and Mg-containing Zn-plated steel sheet is not particularly limited and can appropriately be selected from known methods such as a pressing, punching, and drawing methods.

The formed article of the black-plated steel sheet exhibiting an excellent ability to maintain a black appearance and an excellent press formability can be produced by the above procedures.

In the production method of the present invention, blackening is conducted using water vapor, and therefore the formed article of the black-plated steel sheet can be produced without applying a load to the environment.

Moreover, in the formed article of the black-plated steel sheet obtained by the production method of the present invention, the black oxide imparting a color tone of black is present not only at the surface of the plating layer but also inside the plating layer. Thus, the formed article of the black-plated steel sheet obtained by the production method of the present invention can maintain the black appearance even when the surface of the plating layer is scraped, and exhibits an excellent ability to maintain a black appearance.

Moreover, the formed article of the black-plated steel sheet obtained by the production method of the present invention does not have a coating film, and therefore spot welding can also be conducted in the same manner as in a usual formed article of the hot-dip Al and Mg-containing Zn-plated steel sheet.

EXAMPLES

The following examples further illustrate the present invention, but the scope of the present invention is not limited to the examples.

Experimental Example 1

A hot-dip Al and Mg-containing Zn-plated steel sheet having a plating layer with a thickness of 3 to 100 μm was prepared from a substrate of SPCC with a sheet thickness of 1.2 mm. The plating bath composition (concentration of Zn, Al, Mg, Si, Ti and B) was changed to prepare 29 kinds of plated steel sheets, each of which had a plating layer with a different composition. The plating bath composition and the plating layer thickness for each of the 29 kinds of prepared plated steel sheets are shown in Table 1. The plating bath composition and the plating layer composition are the same.

TABLE 1 Plating layer Plated steel Plating bath composition (mass %) thickness sheet No. Al Mg Si Ti B (μm) 1 6.0 0.1 — — — 15 2 3.8 0.8 — — — 3 6.0 1.1 — — — 4 1.8 1.3 0.006 0.002 — 5 3.8 0.8 0.005 — — 6 3.8 0.8 0.020 — — 7 3.8 0.8 0.200 — — 8 3.8 0.8 2.000 — — 9 3.8 0.8 — 0.001 — 10 3.8 0.8 — 0.002 — 11 3.8 0.8 — 0.100 — 12 3.8 0.8 — — 0.0005 13 3.8 0.8 — — 0.045  14 3.8 0.8 — 0.001 0.0005 15 3.8 0.8 — 0.001 0.045  16 3.8 0.8 — 0.100 0.0005 17 3.8 0.8 — 0.100 0.045  18 3.8 0.8 — 0.002 0.0005 19 3.8 0.8 0.020 0.020 — 20 3.8 0.8 0.020 0.020 0.0005 21 0.1 0.8 — — — 22 22.0 0.8 — — — 23 3.8 0.8 — — — 3 24 3.8 0.8 — — — 10 25 3.8 0.8 — — — 100 26 — 0.2 — — — 15 27 30.0 0.8 — — — 28 6.0 — — — — 29 6.0 15.0  — — —

FIG. 1A is an electron microscope photograph illustrating a cross section of the plating layer of the plated steel sheet No. 2. In FIG. 1A, “A” denotes a part corresponding to the Zn phase, “B” denotes a part corresponding to the Zn/Al phase, and “C” denotes a part corresponding to the Al/Zn/Zn₂Mg phase.

Each prepared plated steel sheet was placed in a high-temperature and high-pressure heat-moisture treatment apparatus (Hisaka Works, Ltd.) to contact the plating layer with water vapor under the conditions shown in Tables 2 and 3. In high-temperature and high-pressure heat-moisture treatment, the conditions to contact the hot-dip Al and Mg-containing Zn-plated steel sheet with water vapor were managed and measured in the following manner. Regarding the temperature, a thermocouple with a protection tube was inserted near the hot-dip Al and Mg-containing Zn-plated steel sheet placed in the high-temperature and high-pressure heat-moisture treatment apparatus, and the value indicated by the thermocouple was recorded. The relative humidity was measured by a wet-bulb thermometer. Regarding the absolute pressure, a small pressure gauge of current signal conversion system was attached at the top section of the high-temperature and high-pressure heat-moisture treatment apparatus, and the value indicated by the pressure gauge was recorded. An auxiliary tank communicating with the high-temperature and high-pressure heat-moisture treatment apparatus through a valve and a pipe was installed for the purpose of measuring an oxygen concentration. The auxiliary tank includes a heating mechanism and a cooling mechanism as the high-temperature and high-pressure heat-moisture treatment apparatus (main body) does. The valve was opened and the atmosphere of the main body was fractionated to the auxiliary tank through the communicating pipe while the temperature of the auxiliary tank was maintained to be the same as that of the main body. Thereafter, the valve was closed, only the auxiliary tank was cooled to normal temperature to condense water vapor, thereby the amount of water condensed from vapor was measured, and the residual gas was analyzed to quantitatively determine the oxygen concentration in the auxiliary tank. The oxygen concentration quantitatively determined was converted to the oxygen concentration in the main body by determining the water vapor concentration in the main body from the measured amount of water.

FIG. 1B is an electron microscope photograph illustrating a cross section of the plating layer of the plated steel sheet of Example 4 after the water vapor treatment. In FIG. 1B, “A” denotes a part corresponding to the Zn phase, “B” denotes a part corresponding to the Zn/Al phase, and “C” denotes a part corresponding to the Al/Zn/Zn₂Mg phase. When FIG. 1A and FIG. 1B are compared, it is understood that changes occur mainly in the Zn/Al phase and in the Al/Zn/Zn₂Mg phase.

The lightness (L* value) of a plating layer surface was measured for each of the plated steel sheets after water vapor treatment (Examples 1 to 40, and Comparative Examples 1 to 11) by spectral reflectance with a spectroscopic color difference meter (TC-1800, made by Tokyo Denshoku Co., Ltd.), in accordance with JIS K 5600. The measurement conditions are shown in the following:

-   -   Optical conditions: d/8° method (double beam optical system)     -   Visual field: 2 degrees     -   Measurement method: reflectometry     -   Standard light: C     -   Color system: CIELAB     -   Measurement wavelength: 380 to 780 nm     -   Measurement wavelength interval: 5 nm     -   Spectroscope: diffraction grating 1,200/mm     -   Lighting: halogen lamp (voltage: 12 V, power: 50 W, rated life:         2,000 hours)     -   Measurement area diameter=7.25 mm     -   Detection element: photomultiplier (R928 made by Hamamatsu         Photonics K.K.)     -   Reflectance: 0 to 150%     -   Measurement temperature: 23° C.     -   Standard plate: white

For each of the plated steel sheets after water vapor treatment (Examples 1 to 40 and Comparative Examples 1 to 11), having an L* value of 35 or less was evaluated as “A”, more than 35 and 40 or less as “B”, more than 40 and 60 or less as “C”, and more than 60 as “D”.

The corrosion resistance was evaluated for each of the plated steel sheets after water vapor treatment (Examples 1 to 40 and Comparative Examples 1 to 11). After sealing the end faces of a sample piece (150 mm long and 70 mm wide) cut out from each of the plated steel sheets, the sample piece was subjected to repeated cycles including a salt water spraying step, a drying step, and a moistening step in one cycle (8 hours). Evaluation was made based on the number of cycles when the proportion of red-rusted area reached 5%. In the salt water spraying step, 5% NaCl aqueous solution at 35° C. was sprayed to the sample piece for 2 hours. In the drying step, the sample piece was left standing for 4 hours in an environment at an atmospheric temperature of 60° C. and a relative humidity of 30%. In the moistening step, the sample piece was left standing for 2 hours in an environment at an atmospheric temperature of 50° C. and a relative humidity of 95%. The sample piece which requires more than 70 cycles for the proportion of red-rusted area to reach 5% was evaluated as “A”, 30 cycles or more and 70 or less as “B”, and less than 30 cycles as “D”.

The lightness and the results of corrosion resistance testing for the plating layer surface of each of the plated steel sheets after water vapor treatment are shown in Tables 2 and 3.

TABLE 2 Corrosion Conditions for contacting with water vapor Blackness resistance Relative Oxygen Absolute Treatment degree Cycle Plated steel sheet Temperature humidity Atmosphere concentration pressure time Lightness number (refer to Table 1) (° C.) (%) gas (%) (MPa) (hour) (L* value) (repeat count) Example 1 1 140 95 None 1 0.34 6 35(A) 30(B) Example 2 1 95 95 Ar 2 0.10 140 35(A) 30(B) Example 3 2 140 95 None 1 0.34 2 42(C) 42(B) Example 4 2 140 95 Ar 1 0.70 2 38(B) 42(B) Example 5 2 80 95 Ar + N₂ 1 0.10 140 36(B) 42(B) Example 6 2 95 95 N₂ 2 0.10 140 33(A) 42(B) Example 7 2 95 95 Ar 2 0.10 140 33(A) 42(B) Example 8 2 95 95 He 2 0.10 140 33(A) 42(B) Example 9 2 140 80 O₂ 6 0.38 6 38(B) 42(B) Example 10 2 140 80 O₂ 10 0.39 6 53(C) 44(B) Example 11 2 140 80 O₂ 13 0.40 6 58(C) 44(B) Example 12 3 140 95 None 1 0.34 6 34(A) 48(B) Example 13 3 95 95 Ar 2 0.10 140 32(A) 48(B) Example 14 4 140 95 None 1 0.34 2 41(C) 48(B) Example 15 4 140 95 Ar 1 0.70 2 38(B) 46(B) Example 16 4 80 95 Ar 1 0.10 140 38(B) 46(B) Example 17 4 95 95 N₂ 2 0.10 140 35(A) 46(B) Example 18 4 95 95 Ar 2 0.10 140 34(A) 46(B) Example 19 4 95 95 He 2 0.10 140 34(A) 46(B) Example 20 5 140 95 None 1 0.34 2 41(C) 42(B) Example 21 6 140 95 None 1 0.34 2 42(C) 42(B) Example 22 7 140 95 None 1 0.34 2 42(C) 42(B) Example 23 8 140 95 None 1 0.34 2 43(C) 42(B) Example 24 9 140 95 None 1 0.34 2 41(C) 42(B) Example 25 10 140 95 None 1 0.34 2 42(C) 42(B)

TABLE 3 Corrosion Conditions for contacting with water vapor Blackness resistance Relative Oxygen Absolute Treatment degree Cycle Plated steel sheet Temperature humidity Atmosphere concentration pressure time Lightness number (refer to Table 1) (° C.) (%) gas (%) (MPa) (hour) (L* value) (repeat count) Example 26 11 140 95 None 1 0.34 2 41(C) 42(B) Example 27 12 140 95 None 1 0.34 2 42(C) 42(B) Example 28 13 140 95 None 1 0.34 2 42(C) 42(B) Example 29 14 140 95 None 1 0.34 2 41(C) 42(B) Example 30 15 140 95 None 1 0.34 2 43(C) 42(B) Example 31 16 140 95 None 1 0.34 2 42(C) 42(B) Example 32 17 140 95 None 1 0.34 2 41(C) 42(B) Example 33 18 140 95 None 1 0.34 2 43(C) 42(B) Example 34 19 140 95 None 1 0.34 2 42(C) 42(B) Example 35 20 140 95 None 1 0.34 2 41(C) 42(B) Example 36 21 140 95 None 1 0.34 2 42(C) 30(B) Example 37 22 140 95 None 1 0.34 2 41(C) 70 < (A) Example 38 23 140 95 None 1 0.34 6 34(A) 30(B) Example 39 24 140 95 None 1 0.34 6 34(A) 38(B) Example 40 25 140 95 None 1 0.34 6 34(A) 70 < (A) Comparative 26 140 95 None 1 0.34 6 38(B) 20(D) Example 1 Comparative 26 95 95 Ar 2 0.10 140 38(B) 20(D) Example 2 Comparative 27 140 95 None 1 0.34 6 25(A) 70 < (A) Example 3 Comparative 27 95 95 N₂ 2 0.10 140 26(A) 70 < (A) Example 4 Comparative 28 140 95 None 1 0.34 6 39(B) 26(D) Example 5 Comparative 28 95 95 Ar 2 0.10 140 39(B) 26(D) Example 6 Comparative 29 140 95 None 1 0.34 6 28(A) 70 < (A) Example 7 Comparative 29 95 95 Ar 2 0.10 140 26(A) 70 < (A) Example 8 Comparative 2 140 80 O₂ 15 0.60 6 62(D) 70 < (A) Example 9 Comparative 2 140 80 O₂ 18 0.60 6 65(D) 48(B) Example 10 Comparative 2 95 95 O₂ 20 0.10 140 71(D) 48(B) Example 11

As shown in Tables 2 and 3, in the plated steel sheets of Comparative Examples 1 and 2, the Al content in the plating layer was out of a proper range, and therefore the corrosion resistance was lowered. In the plated steel sheets of Comparative Examples 5 and 6, the Mg content in the plating layer was out of a proper range, and therefore the corrosion resistance was lowered. Moreover, in the plated steel sheets of Comparative Examples 3, 4, 7, and 8, the amount of an oxide (dross) generated at the surface of the plating bath became large and the dross was adhered to the surface of the plating layer in producing the plated steel sheet, and therefore beautiful plating was not obtained. In the plated steel sheets of Comparative Examples 9 to 11, the oxygen concentration during the water vapor treatment was high, and therefore blackening was not able to be conducted sufficiently. In contrast, the plated steel sheets of Examples 1 to 40 were sufficiently blackened and the corrosion resistance of the plating layers was favorable.

Moreover, the adhesion of the plating layer was also evaluated for each plated steel sheet after the water vapor treatment. The evaluation of the adhesion was conducted by cutting out a test piece from each plated steel sheet after the water vapor treatment, bending the test piece by 180° (8 t), and conducting a cellophane tape peeling test for the bent portion. In any of the plated steel sheets of Examples 1 to 40, the peeled area ratio was 10% or less, and it was confirmed that favorable processing adhesion was maintained even after the water vapor treatment.

It is understood from the above results that the method for producing a black-plated steel sheet of the present invention can produce a black-plated steel sheet exhibiting an excellent ability to maintain a black appearance and an excellent press formability.

Experimental Example 2

Each of the plated steel sheets of Nos. 1 to 3 in Table 1 was placed in an incubator (PV(H)-331; ESPEC CORP.) and was preheated in the atmosphere under the conditions shown in table 4. Next, the preheated plated steel sheet was placed in the high-temperature and high-pressure heat-moisture treatment apparatus to contact the plating layer with water vapor under the conditions shown in Table 4.

The surface lightness (L* value) of the plating layer for each plated steel sheet after the water vapor treatment (Examples 41 to 51) was measured using the spectroscopic color-difference meter. The lightness for the plating layer surface of each of the plated steel sheets after water vapor treatment is shown in Table 4.

TABLE 4 Conditions for contacting with water vapor Blackness Preheating Relative Oxygen Absolute Treatment degree Plated steel sheet Temperature Time Temperature humidity Atmosphere concentration pressure time Lightness (refer to Table 1) (° C.) (hours) (° C.) (%) gas (%) (MPa) (hour) (L* value) Example 41 2 None 145 85 None 4 0.35 1 48(C) Example 42 2 None 95 95 Ar 1 0.10 48 50(C) Example 43 2 200 10 145 85 None 4 0.35 1 37(B) Example 44 2 200 6 145 85 None 4 0.35 1 39(B) Example 45 2 200 2 145 85 None 4 0.35 1 43(C) Example 46 2 200 1 145 85 None 4 0.35 1 45(C) Example 47 2 250 6 95 95 Ar 1 0.10 48 39(B) Example 48 1 None 145 85 None 4 0.35 1 52(C) Example 49 1 200 10 145 85 None 4 0.35 1 39(B) Example 50 3 None 145 85 None 4 0.35 1 48(C) Example 51 3 200 10 145 85 None 4 0.35 1 38(B)

As shown in Table 4, in the plated steel sheets of Examples 43 to 47, 49, and 51 to which preheating was conducted before the water vapor treatment, the lightness was lowered even by the treatment in a short time as compared with the lightness of the plated steel sheets to which preheating was not conducted.

It is understood from the above results that the time required for the water vapor treatment can be shortened by conducting preheating before the water vapor treatment.

Experimental Example 3

From each of the plated steel sheets of Nos. 1, 2, and 4 in Table 1, 7 test pieces (500 mm×500 mm) were cut out. Moreover, from polypropylene nonwoven fabric having a thickness of about 0.7 mm, 9 planar spacers (450 mm×450 mm) were cut out. As illustrated in FIG. 2, a laminated body including 21 test pieces (plated steel sheets) and 9 spacers (nonwoven fabric) was formed. Looking at the plated steel sheet No. 1, there are 3 parts where the plated steel sheets are directly contacted with each other, and there are 3 parts where the spacer is held between the plated steel sheets. Also in each of the plated steel sheets Nos. 2 and 4, there are 3 parts where the plated steel sheets are directly contacted with each other, and there are 3 parts where the spacer is held between the plated steel sheets.

The laminated body was placed in the high-temperature and high-pressure heat-moisture treatment apparatus, and the water vapor treatment was conducted under the conditions shown in Table 5.

TABLE 5 Oxygen Temper- Relative Atmo- concen- Absolute Treatment Con- ature humidity sphere tration pressure time dition (° C.) (%) gas (%) (MPa) (hour) A 115 95 None 1 0.34 36 B Ar 0.70 24 C N₂ 0.70 24

The uniformity of blackening and the corrosion resistance were evaluated for each test piece after the water vapor treatment. First of all, the laminated body was disassembled, and, for each plated steel sheet, the test pieces (3 pieces in the lower side in FIG. 2) subjected to the water vapor treatment in a state where the spacer was not held between the plated steel sheets and the test pieces (3 pieces in the upper side in FIG. 2) subjected to the water vapor treatment in a state where the spacer was held between the plated steel sheets were taken out.

The lightness (L* value) at the peripheral parts (arbitrary 4 parts located at 20 mm inside from the edge per test piece) and the central parts (arbitrary 4 parts located near the center per test piece) was measured using the spectroscopic color-difference meter for each of the 3 test pieces the water vapor treatment conditions of which were the same. The average value of 3 pieces was calculated for each of the peripheral parts and the central parts. And the difference, ΔL* value, of the average value of the L* values at the central parts and the average value of the L* values at the peripheral parts was used as an evaluation index of the uniformity of blackening. Each test piece was evaluated as “A” in the case where the ΔL* value was 5 or less, “B” in the case where the ΔL* value was more than 5 and 10 or less, “C” in the case where the ΔL* value was more than 10 and 15 or less, and “D” in the case where the ΔL* value was more than 15.

Moreover, a 70 mm×150 mm test piece was cut out from the central part of each test piece, and the corrosion resistance was evaluated in the same procedures as in Experimental Example 1.

The surface lightness of the plating layer and the corrosion resistance test result for each test piece after the water vapor treatment are shown in Table 6.

TABLE 6 Corrosion Blackness degree resistance Peripheral part Central part Lightness Cycle Water vapor treatment Plated steel sheet lightness lightness difference number Condition Spacer (refer to Table 1) (L* value) (L* value) (ΔL* value) (repeat count) Example 52 A Present 1 36 37  1(A) 30(B) Example 53 A Absent 1 37 79 42(D) 36(B) Example 54 A Present 2 33 34  1(A) 42(B) Example 55 A Absent 2 34 77 43(D) 47(B) Example 56 A Present 4 32 33  1(A) 48(B) Example 57 A Absent 4 32 79 47(D) 52(B) Example 58 B Present 1 36 37  1(A) 30(B) Example 59 B Absent 1 38 79 41(D) 36(B) Example 60 B Present 2 33 34  1(A) 42(B) Example 61 B Absent 2 35 78 43(D) 48(B) Example 62 B Present 4 32 33  1(A) 49(B) Example 63 B Absent 4 33 77 44(D) 52(B) Example 64 C Present 1 36 37  1(A) 30(B) Example 65 C Absent 1 37 79 42(D) 36(B) Example 66 C Present 2 33 35  2(A) 43(B) Example 67 C Absent 2 33 78 45(D) 47(B) Example 68 C Present 4 32 34  2(A) 48(B) Example 69 C Absent 4 33 78 45(D) 52(B)

As shown in Table 6, in the test pieces (Examples 53, 55, 57, 59, 61, 63, 65, 67, and 69) each subjected to the water vapor treatment in a state where the spacer was not held between the plated steel sheets, the blackness at the peripheral parts was sufficient, however the blackness at the central parts was insufficient. The reason is considered that the test pieces are contacted with each other without a gap and a sufficient amount of water vapor was not able to reach the central parts. On the other hand, in the test pieces (Examples 52, 54, 56, 58, 60, 62, 64, 66, and 68) each subjected to the water vapor treatment in a state where the spacer was held between the plated steel sheets, not only the peripheral parts but also the central parts were sufficiently blackened, and the uniformity of blackening was also favorable. In these test pieces, traces of the spacer were not left.

It is understood from the above results that a black-plated steel sheet exhibiting an excellent appearance and an excellent corrosion resistance can be produced by holding the spacer between the plated steel sheets even in the case where the water vapor treatment is conducted simultaneously to a plurality of plated steel sheets.

Experimental Example 4

Each inorganic chemical treatment liquid shown in Table 7 was applied to the plated steel sheet No. 2 in Table 1, and the plated steel sheet was put into an electric oven without washing with water, and then heated and dried in a condition where the end-point temperature of the plate was to be 120° C. to form an inorganic coating film on the surface of the plated steel sheet.

TABLE 7 Valve metal compound Phosphate Organic acid Treatment Concentration Concentration Concentration liquid No. Type (g/L) Type (g/L) Type (g/L) 1 H₂TiF₆ Ti: 2 H₃PO₄ P: 4 — — 2 (NH₄)₂TiF₆ Ti: 6 H₃PO₄ P: 4 — — 3 H₂TiF₆ Ti: 8 — — Tannic acid 10 4 (NH₄)VO₃ V: 5 — — — — 5 V₂O₅ V: 5 H₃PO₄ P: 4 — — (NH₄)₂ZrO(CO₃)₂ Zr: 6 6 H₂ZrF₆ Zr: 6 — — — — 7 Zr(SO₄)₂ Zr: 6 — — — — 8 HfF₄ Hf: 1 — — — — 9 H₂SiF₆ Si: 2 H₃PO₄ P: 4 — — 10 Al(NO₃)₃•9H₂O Al: 1 — — — — 11 (NH₄)₁₀W₁₂O₄₁ W: 3 — — — — 12 Niobic acid sol Nb: 2 — — Tartaric acid 10 13 Ta₂O₅•nH₂O Ta: 1 — — — — 14 V₂O₅ V: 5 H₃PO₄ P: 4 — — ZrO(NO₃)₂•2H₂O Zr: 6 15 ZrO(NO₃)₂•2H₂O Zr: 10 — — — —

The plated steel sheet on which the inorganic coating film was formed was placed in the high-temperature and high-pressure heat-moisture treatment apparatus to contact the plating layer with water vapor under the conditions shown in Table 8.

The surface lightness (L* value) of the plating layer for each plated steel sheet (Examples 70 to 85) after the water vapor treatment was measured using the spectroscopic color-difference meter. Moreover, the corrosion resistance test for each plated steel sheet (Examples 70 to 85) after the water vapor treatment was also conducted. The corrosion resistance test was conducted by spraying a NaCl aqueous solution having a temperature of 35° C. to the test piece for 12 hours in accordance with JIS Z2371. The case where the area ratio of the white rust generation after spraying was 0% was evaluated as “A,” the case of more than 0% and 5% or less was evaluated as “B,” the case of more than 5% and 10% or less was evaluated as “C,” and the case of more than 10% was evaluated as “D.”

The surface lightness of the plating layer and the corrosion resistance test result for each plated steel sheet after the water vapor treatment are shown in Table 8.

TABLE 8 Inorganic treatment Conditions for contacting with water vapor Corrosion Plated Treatment Oxygen Blackness resistance steel sheet liquid No. Attachment amount Temper- Relative concen- Absolute Treatment degree White-rusted (refer to (refer to of valve metal ature humidity tration pressure time Lightness area ratio Table 1) Table 7) (mg/m²) (° C.) (%) (%) (MPa) (hour) (L* value) (%) Example 70 2 1 Ti: 60 110 80 4 0.12 24 37(B) 0(A) Example 71 2 Ti: 70 35(A) 0(A) Example 72 3 Ti: 80 37(B) 0(A) Example 73 4 V: 50 36(B) 0(A) Example 74 5 V: 50 35(A) 0(A) Zr: 60 Example 75 6 Zr: 100 36(B) 0(A) Example 76 7 Zr: 60 37(B) 0(A) Example 77 8 Hf: 100 37(B) 0(A) Example 78 9 Si: 200 36(B) 0(A) Example 79 10 Al: 150 35(A) 0(A) Example 80 11 W: 90 36(B) 0(A) Example 81 12 Nb: 80 37(B) 0(A) Example 82 13 Ta: 70 36(B) 0(A) Example 83 14 V: 60 37(B) 0(A) Zr: 72 Example 84 15 Zr: 100 36(B) 0(A) Example 85 None 35(A) 96(D) 

As shown in Table 8, the plated steel sheets of Examples 70 to 84 on which the inorganic coating film was formed exhibited more excellent corrosion resistance as compared with the plated steel sheet of Example 85 on which the inorganic coating film was not formed.

It is understood from the above results that the corrosion resistance of a black-plated steel sheet can be improved by forming the inorganic coating film.

Experimental Example 5

The plated steel sheet No. 2 in Table 1 was placed in the high-temperature and high-pressure heat-moisture treatment apparatus, and the plating layer was contacted with water vapor under the conditions shown in Table 9 to obtain a black-plated steel sheet.

TABLE 9 Conditions for contacting with water vapor Blackness Relative Oxygen Absolute Treatment degree Black-plated Plated steel sheet Temperature humidity concentration pressure time Lightness steel sheet No. (refer to Table 1) (° C.) (%) (%) (MPa) (hour) (L* value) A 2 110 85 3 0.12 28 34(A)

Each organic chemical treatment liquid shown in Table 10 was applied to the obtained black-plated steel sheet, and the black-plated steel sheet was put into an electric oven without washing with water, and then heated and dried in a condition where the end-point temperature of the plate was to be 160° C. to form an organic resin coating film on the surface of the plated steel sheet.

TABLE 10 Organic resin Lubricant Valve metal compound Phosphate Organic acid Treatment Concen- Concen- Concen- Concen- Concen- liquid tration tration tration tration tration No. Type (g/L) (g/L) Type (g/L) Type (g/L) Type (g/L) 1 Urethane resin 100 — H₂TiF₆ Ti: 1 H₃PO₄ P: 1 — — 2 Epoxy resin 100 — (NH₄)₂TiF₆ Ti: 1 H₃PO₄ P: 1 — — 3 Urethane resin 100 — H₂TiF₆ Ti: 1 — — — — 4 Acrylic resin 100 — (NH₄)VO₃ V: 1 — — — — 5 Urethane resin 100 — V₂O₅ V: 1 H₃PO₄ P: 1 — — (NH₄)₂ZrO(CO₃)₂ Zr: 1 6 Urethane resin 100 5 V₂O₅ V: 1 H₃PO₄ P: 1 — — (Na₄)₂ZrO(CO₃)₂ Zr: 1 7 Polyolefin resin 100 — Zr(SO₄)₂ Zr: 1 — — — — 8 Acrylic resin 100 — HfF₄ Hf: 1 — — — — 9 Urethane resin 100 — H₂SiF₆ Si: 1 H₃PO₄ P: 1 — — 10 Fluorine resin 100 — Al(NO₃)₃•9H₂O Al: 1 — — — — 11 Polyester resin 100 — — — — — Tannic acid 10 12 Urethane resin 100 — Niobic acid sol Nb: 1 — — — — 13 Urethane resin 100 — Ta₂O₅•nH₂O Ta: 1 — — — — 14 Acrylic resin 100 — V₂O₅ V: 1 H₃PO₄ P: 1 — — ZrO(NO₃)₂•2H₂O Zr: 1 15 Urethane resin 100 — ZrO(NO₃)₂•2H₂O Zr: 1 — — — — Lubricant: polyethylene-based wax (average particle diameter:: 1.0 μm)

The corrosion resistance test and the galling resistance test were conducted for each plated steel sheet (Examples 86 to 101) on which the organic resin coating film was formed. The corrosion resistance test was conducted by spraying a NaCl aqueous solution having a temperature of 35° C. to the test piece for 12 hours in accordance with JIS Z2371. In the galling resistance testing, a 30-mm by 250-mm sample piece was subjected to a bead drawing test (bead height: 4 mm, applied pressure: 3.0 kN), and the sliding surface was visually observed after testing. The sample piece with a proportion of scratched area in the sliding surface of 0% (no scratch) was evaluated as “A”, more than 0% and less than 5% as “B”, 5% or more and less than 10% as “C”, and 10% or more as “D”.

The results of the corrosion resistance testing and the galling resistance testing for each plated steel sheet are shown in Table 11.

TABLE 11 Corrosion Black- resistance Galling plated Organic treatment White- resistance steel sheet Treatment Film rusted Scratched (refer to No. (refer to thickness area ratio area ratio Table 9) Table 10) (μm) (%) (%) Example 86 A 1 2  0(A)  6(C) Example 87 2 2  0(A)  9(C) Example 88 3 2  0(A)  5(C) Example 89 4 2  0(A)  6(C) Example 90 5 2  0(A)  4(B) Example 91 6 2  0(A)  0(A) Example 92 7 2  0(A)  5(C) Example 93 8 2  0(A)  6(C) Example 94 9 2  0(A)  3(B) Example 95 10 2  0(A)  3(B) Example 96 11 2  0(A)  6(C) Example 97 12 2  0(A)  4(B) Example 98 13 2  0(A)  4(B) Example 99 14 2  0(A)  6(C) Example 100 15 2  0(A)  3(B) Example 101 None 98(D) 92(D)

As shown in Table 11, the plated steel sheets of Examples 86 to 100 on which the organic resin coating film was formed exhibited more excellent corrosion resistance and galling resistance as compared with the plated steel sheet of Example 101 on which the organic resin coating film was not formed.

It is understood from the above results that the corrosion resistance and the galling resistance of a black-plated steel sheet can be improved by forming the organic resin coating film.

Experimental Example 6

A plated steel sheet No. 2 in Table 1 was coated with an organic chemical treatment liquid shown in Table 12, and placed in an electric oven without washing with water so as to be heated and dried under conditions for the plate temperature to reach 160° C. Consequently an organic resin coating film (urethane-based resin coating film) was formed on the surface of the plated steel sheet. The ether-based polyol for use was polypropylene glycol. The ester-based polyol for use was adipic acid. The polyisocyanate for use was hydrogenated tolylenediisocyanate.

TABLE 12 Urethane-based resin Valve metal compound Phosphate Polyvalent phenol Treatment Polyol ratio (mass %) Concen- Concen- Concen- Concen- liquid Ether-based Ester-based tration tration tration tration No. (polypropylene glycol) (adipic acid) (g/L) Type (g/L) Type (g/L) Type (g/L) 16 5 95 100 — — — — — — 17 5 95 100 H₂TiF₆ Ti: 1 H₃PO₄ P: 1 — — 18 5 95 100 (NH₄)VO₃ V: 1 H₃PO₄ P: 1 — — 19 5 95 100 ZrO(NO₃)₂•2H₂O Zr: 1 — — — — 20 5 95 100 HfF₄ Hf: 1 — — — — 21 5 95 100 H₂SiF₆ Si: 1 — — — — 22 5 95 100 Niobic acid sol Nb: 1 — — — — 23 5 95 100 Al(NO₃)•9H₂O Al: 1 — — — — 24 5 95 100 Ta₂O₅•nH₂O Ta: 1 — — — — 25 5 95 100 V₂O₅ V: 1 H₃PO₄ P: 1 — — 26 5 95 100 — — — — Tannic acid 10 27 30 70 100 — — — — — — 28 30 70 100 (NH₄)VO₃ V: 1 H₃PO₄ P: 1 — — 29 30 70 100 V₂O₅ V: 1 H₃PO₄ P: 1 — — 30 30 70 180 ZrO(NO₃)₂•2H₂O Zr: 1 — — — — 31 30 70 100 — — — — Tannic acid 10 32 0 100 100 — — — — — — 33 0 100 100 (NH₄)VO₃ V: 1 H₃PO₄ P: 1 — — 34 0 100 100 V₂O₅ V: 1 H₃PO₄ P: 1 — — 35 0 100 100 ZrO(NO₃)₂•2H₂O Zr: 1 — — — — 36 0 100 100 — — — — Tannic acid 10 37 2 98 100 — — — — — — 38 35 65 100 — — — — — — 39 2 98 100 — — — — Tannic acid 10 40 35 65 100 — — — — Tannic acid 10

The plated steel sheet having the organic resin coating film was placed in a high-temperature and high-pressure heat-moisture treatment apparatus, and the plating layer was contacted with water vapor under the conditions shown in Table 13.

The surface lightness (L* value) of the plating layer for each plated steel sheet (Examples 102 to 126) after the water vapor treatment was measured using the spectroscopic color-difference meter. Moreover, the corrosion resistance test was also conducted for each plated steel sheet (Examples 102 to 126) after the water vapor treatment.

The surface lightness of the plating layer and the corrosion resistance test result for each plated steel sheet after the water vapor treatment are shown in Table 13.

TABLE 13 Organic treatment Conditions for contacting with water vapor Corrosion Treatment Oxygen Blackness resistance liquid No. Film Temper- Relative concen- Absolute Treatment degree White-rusted Plated steel sheet (refer to thickness ature humidity tration pressure time Lightness area ratio (refer to Table 1) Table 12) (μm) (° C.) (%) (%) (MPa) (hour) (L* value) (%) Example 102 2 16 2 110 90 4 0.13 21 31(A) 9(C) Example 103 17 2 33(A) 6(C) Example 104 18 2 32(A) 5(B) Example 105 19 2 31(A) 4(B) Example 106 20 2 32(A) 3(B) Example 107 21 2 32(A) 4(B) Example 108 22 2 32(A) 6(C) Example 109 23 2 31(A) 4(B) Example 110 24 2 33(A) 6(C) Example 111 25 2 32(A) 4(B) Example 112 26 2 33(A) 0(A) Example 113 27 2 31(A) 9(C) Example 114 28 2 31(A) 3(B) Example 115 29 2 31(A) 3(B) Example 116 30 2 31(A) 3(B) Example 117 31 2 30(A) 0(A) Example 118 32 2 33(A) 35(D)  Example 119 33 2 32(A) 25(D)  Example 120 34 2 31(A) 26(D)  Example 121 35 2 31(A) 15(D)  Example 122 36 2 31(A) 33(D)  Example 123 37 2 32(A) 18(D)  Example 124 38 2 32(A) 20(D)  Example 125 39 2 32(A) 12(D)  Example 126 40 2 31(A) 13(D) 

In the present Experimental Example, the organic resin coating film was formed on the hot-dip Al and Mg-containing Zn-plated steel sheet, and thereafter the plated steel sheet on which the organic resin coating film was formed was contacted with water vapor to blacken. In this case, it sometimes occurs that the corrosion resistance cannot sufficiently be improved even when the organic resin coating film is formed (see, Examples 118 to 126). In contrast, the corrosion resistance of the black-plated steel sheets of Examples 102 to 117 on which a resin coating film of a urethane resin obtained by combining an ether-based polyol and an ester-based polyol in a predetermined ratio was formed has sufficiently been improved.

This application claims the benefit of Japanese Patent Application No. 2012-100440, filed on Apr. 25, 2012 and Japanese Patent Application No. 2013-062220, filed on Mar. 25, 2013, the disclosure of which including the specifications and drawings is incorporated herein by reference in its entirety.

INDUSTRIAL APPLICABILITY

The black-plated steel sheet of the present invention exhibits excellent design property, ability to maintain a black appearance, press formability, and corrosion resistance and therefore is useful as a plated steel sheet to be used for, for example, a roof material or exterior material of a building, an electric appliance, an automobile, or the like. 

1. A method for producing a black-plated steel sheet, comprising: providing a hot-dip Al and Mg-containing Zn-plated steel sheet comprising a hot-dip Al and Mg-containing Zn-plated layer which comprises 0.1 mass % or more and 22.0 mass % or less of Al and 0.1 mass % or more and less than 1.5 mass % of Mg; and contacting the hot-dip Al and Mg-containing Zn-plated steel sheet with water vapor in a closed vessel, wherein: an oxygen concentration in the closed vessel is 13% or less.
 2. The method for producing a black-plated steel sheet according to claim 1, further comprising forming an inorganic coating film on a surface of the hot-dip Al and Mg-containing Zn-plated steel sheet.
 3. The method for producing a black-plated steel sheet according to claim 2, wherein the inorganic coating film comprises one or more compounds selected from the group consisting of an oxide of valve metal, an oxoate of valve metal, a hydroxide of valve metal, a phosphate of valve metal, and a fluoride of valve metal, the valve metal is one or more metals selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, W, Si and Al.
 4. (canceled)
 5. The method for producing a black-plated steel sheet according to claim 1, further comprising forming an organic resin coating film on a surface of the hot-dip Al and Mg-containing Zn-plated steel sheet.
 6. The method for producing a black-plated steel sheet according to claim 5, wherein: an organic resin comprised in the organic resin coating film is urethane-based resin obtained by the reaction of polyols consisting of an ether-based polyol and an ester-based polyol with polyisocyanate, a proportion of the ether-based polyol in the polyols being 5 to 30 mass %.
 7. The method for producing a black-plated steel sheet according to claim 6, wherein the organic resin coating film further comprises a polyvalent phenol.
 8. The method for producing a black-plated steel sheet according to claim 5, wherein the organic resin coating film comprises a lubricant.
 9. The method for producing a black-plated steel sheet according to claim 5, wherein the organic resin coating film comprises one or more compounds selected from the group consisting of an oxide of valve metal, an oxoate of valve metal, a hydroxide of valve metal, a phosphate of valve metal, and a fluoride of valve metal, the valve metal is one or more metals selected from the group consisting of Ti, Zr, Hf, V, Nb, Ta, W, Si, and Al.
 10. (canceled)
 11. The method for producing a black-plated steel sheet according to claim 5, wherein the organic resin coating film is a laminate layer or a coating layer.
 12. The method for producing a black-plated steel sheet according to claim 5, wherein the organic resin coating film is a clear coating film.
 13. A method for producing a formed article of a black-plated steel sheet, comprising: providing a hot-dip Al and Mg-containing Zn-plated steel sheet comprising a hot-dip Al and Mg-containing Zn-plated layer which comprises 0.1 mass % or more and 22.0 mass % or less of Al and 0.1 mass % or more and less than 1.5 mass % of Mg; contacting the hot-dip Al and Mg-containing Zn-plated steel sheet with water vapor in a closed vessel; and forming the hot-dip Al and Mg-containing Zn-plated steel sheet before or after contacting the hot-dip Al and Mg-containing Zn-plated steel sheet with the water vapor, wherein: an oxygen concentration in the closed vessel is 13% or less. 